PRESSURE EQUIPMENT MADE FROM BOROSILICATE GLASS 3.3 - GENERAL RULES FOR DESIGN, MANUFACTURE AND TESTING
Hardcopy , PDF
German, English
01-01-1997
Vorwort
Einleitung
1 Anwendungsbereich
2 Normative Verweisungen
3 Symbole und Einheiten
4 Werkstoff
5 Bestätigung der Qualitätskennwerte
6 Festigkeitskennwerte für die Ausführung
7 Berechnung
8 Kennzeichnung
9 Inspektion und Prüfung
Defines material, design, inspection, testing and marking requirements made from borosilicate glass 3.3 having a coefficient of mean linear thermal expansion of (3,3+-0,1) X 10-6 K-1. Does not apply to circular, flat and tubular sight glasses or equipment made from borosilicate glass with another coefficient of thermal expansion.
| DocumentType |
Standard
|
| Pages |
7
|
| PublisherName |
German Institute for Standardisation (Deutsches Institut für Normung)
|
| Status |
Current
|
| Standards | Relationship |
| I.S. EN 1595:1997 | Identical |
| NEN EN 1595 : 1997 | Identical |
| NF EN 1595 : 1997 | Identical |
| NS EN 1595 : 1ED 1997 | Identical |
| NBN EN 1595 : 1997 | Identical |
| BS EN 1595:1997 | Identical |
| EN 1595:1997 | Identical |
| UNE-EN 1595:1997 | Equivalent |
| ISO 720:1985 | Glass — Hydrolytic resistance of glass grains at 121 degrees C — Method of test and classification |
| ISO 695:1991 | Glass — Resistance to attack by a boiling aqueous solution of mixed alkali — Method of test and classification |
| DIN ISO 1776:1988-05 | GLASS - RESISTANCE TO ATTACK BY HYDROCHLORIC ACID AT 100 DEGREES C - FLAME EMISSION OR FLAME ATOMIC ABSORPTION SPECTROMETRIC METHOD |
| DIN ISO 720:1989-12 | Glass; Hydrolytic resistance of glass grains at 121 ?C; method of test and classification; identical with ISO 720:1985 |
| DIN ISO 695:1994-02 | GLASS - RESISTANCE TO ATTACK BY A ROLLING AQUEOUS SOLUTION OF MIXED ALKALI - METHOD OF TEST AND CLASSIFICATION |
| ISO 7884-8:1987 | Glass — Viscosity and viscometric fixed points — Part 8: Determination of (dilatometric) transformation temperature |
| ISO 1776:1985 | Glass — Resistance to attack by hydrochloric acid at 100 degrees C — Flame emission or flame atomic absorption spectrometric method |
| ISO 719:1985 | Glass — Hydrolytic resistance of glass grains at 98 degrees C — Method of test and classification |
| ISO 7991:1987 | Glass — Determination of coefficient of mean linear thermal expansion |
| DIN ISO 719:1989-12 | Glass; hydrolytic resistance of glass grains at 98 ?C; method of test and classification; identical with ISO 719:1985 |
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : All end users must be registered with an Account prior to user licenses being assigned.
Users cannot be edited or removed once added to your Multi user PDF.