BS L 103:1971
Withdrawn
Specification for forging stock and forgings of aluminium-copper-magnesium-silicon-manganese alloy (solution treated and aged at room temperature) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8)
Hardcopy , PDF
English
08-31-1971
09-27-2012
NO CONTENTS SECTION
Describes manufacture, inspection and testing of heat resisting alloys for aerospace purposes. Gives chemical composition and mechanical properties. This covers forging stock and forgings of aluminium copper magnesium silicon manganese alloy.
| Committee |
ACE/61/-/24
|
| DevelopmentNote |
Supersedes BS L76(1959) & 69/23023 DC. (07/2004) Inactive for the new design. (12/2007)
|
| DocumentType |
Standard
|
| Pages |
8
|
| PublisherName |
British Standards Institution
|
| Status |
Withdrawn
|
| Supersedes |
| BS 3L 63:1971 | Specification for tube of aluminium-copper-mangesium-silicon-manganese alloy (solution treated and precipitation treated) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8) |
| BS 2L 77:1971 | Specification for forging stock and forgings of aluminium-copper-magnesium-silicon-manganese alloy (solution treated and precipitation treated) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8) |
| BS L 102:1971 | Specification for bars and extruded sections of aluminium-copper-magnesium-silicon-manganese alloy (solution treated and aged at room temperature) (not exceeding 200 mm diameter or minor sectional dimension) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8) |
| BS 2L 87:1971 | Specification for hexagonal bars for nuts, couplings and hollow machined parts of aluminium-copper-magnesium-silicon-manganese alloy (solution treated and precipitation treated) (free from peripheral and asymmetric coarse grain) (not less than 14 mm nor more than 36 mm across flats) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8) |
| BS 2L 93:1971 | Specification for plate of aluminium-copper-magnesium-silicon-manganese alloy (solution treated, controlled stretched and precipitation treated) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8) |
| BS L 105:1971 | Specification for tube of aluminium-copper-magnesium-silicon-manganese alloy (solution treated and aged at room temperature) (not exceeding 10 mm wall thickness) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8) |
| BS L108(1971) : LATEST | |
| BS L104(1971) : LATEST | |
| BS 3763:1976 | The International System of units (SI) |
| BS L 102:1971 | Specification for bars and extruded sections of aluminium-copper-magnesium-silicon-manganese alloy (solution treated and aged at room temperature) (not exceeding 200 mm diameter or minor sectional dimension) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8) |
| BS L107(1971) : LATEST | |
| BS L 105:1971 | Specification for tube of aluminium-copper-magnesium-silicon-manganese alloy (solution treated and aged at room temperature) (not exceeding 10 mm wall thickness) (Cu 4.4, Mg 0.5, Si 0.7, Mn 0.8) |
| BS L106(1971) : LATEST | |
| BS 350:2004 | Conversion factors for units |
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : All end users must be registered with an Account prior to user licenses being assigned.
Users cannot be edited or removed once added to your Multi user PDF.