ANODIZING OF TITANIUM AND TITANIUM ALLOYS
Published date
01-12-2013
Publisher
Withdrawn date
04-01-1999
Sorry this product is not available in your region.
Covers the requirements for the anodic oxidation of titanium and titanium alloy aerospatial parts primarily for the prevention of seizure, with or without the subsequent application of a heat cured solid film lubricant coating to the requirements of DEFSTAN 91-19/1.
| DevelopmentNote |
This standard was declared obsolescent on 1 April '99 It will no longer be updated but will be retained to provide for the servicing of existing equipment
|
| DocumentType |
Standard
|
| PublisherName |
Ministry of Defence (UK) Standards
|
| Status |
Withdrawn
|
| BS A266-271(1977) : 1977 AMD 2811 | SPECIFICATION FOR 100 DEGREES COUNTERSUNK HEAD TITANIUM ALLOY BOLTS 160000 LBF/IN[2] (1100 MPA) WITH HI-TORQUE SPEED DRIVE RECESSES |
| 15/30329889 DC : 0 | BS A 266 TO 271 - BOLT, 100 DEGREES COUNTERSUNK HEAD, HI-TORQUE SPEED DRIVE RECESS, UNJF THREAD, SPLIT PIN HOLE OPTION, TITANIUM ALLOY, VARIOUS FINISHES, CLASSIFICATION: 80 TF/IN[2] (1100 MPA) AT TA/+315 DEGREES C |
| BS 2A 266 to 2A 271:2016+A1:2019 | Aerospace Series. Bolt, 100° Countersunk head, Hi-Torque speed drive recess, close tolerance shank, UNJF thread, split pin hole option, titanium alloy, various finishes. Classification: R<sub>m</sub> 1100–1250 MPa (160 000–180 000 lbf/in<sup>2</sup>) at Ambient Temperature | +315 °C |
| BS A254-259(1976) : 1976 | HEXAGONAL HEAD TITANIUM ALLOY BOLTS 160000 LBF/IN[2] (1100 MPA) |
| DEFSTAN 03-30(PT5)/1(1992) : 1992 | TREATMENTS FOR THE PROTECTION OF METAL PARTS OF SERVICE STORES AND EQUIPMENT AGAINST CORROSION - PART 5: INDEX, RELATED DOCUMENTS AND SOURCES |
Summarise
Sorry this product is not available in your region.