EN ISO 13807:2009
Withdrawn
Vitreous and porcelain enamels - Determination of crack formation temperature in the thermal shock testing of enamels for the chemical industry (ISO 13807:1999, including Cor 1:2000)
01-14-2009
07-31-2009
Foreword
1 Scope
2 Normative references
3 Terms and definitions
4 Designation
5 Principle
6 Apparatus
7 Specimens
8 Procedure
9 Expression of results
10 Test report
Annex A (informative) Explanatory notes
Bibliography
This International Standard specifies a test method for the determination of the crack formation temperature ofenamels for the chemical industry by subjecting enamelled steel specimens to thermal shock using cold water.The value of the crack formation temperature measured according to this test method is not valid for the finishedcomponent (see annex A). It is a parameter of vitreous and porcelain enamels for comparing the relative quality ofdifferent enamel formulations.
| Committee |
CEN/TC 262
|
| DocumentType |
Standard
|
| PublisherName |
Comite Europeen de Normalisation
|
| Status |
Withdrawn
|
| Standards | Relationship |
| DS EN ISO 13807 : 2009 | Identical |
| NEN EN ISO 13807 : 2009 | Identical |
| PN EN ISO 13807 : 2009 | Identical |
| BS EN ISO 13807:2009 | Identical |
| ISO 13807:1999 | Identical |
| I.S. EN ISO 13807:2009 | Identical |
| NS EN ISO 13807 : 2009 | Identical |
| NBN EN ISO 13807 : 2009 | Identical |
| NF EN ISO 13807 : 2009 | Identical |
| DIN EN ISO 13807:2009-04 | Identical |
| UNE-EN ISO 13807:2009 | Identical |
| ISO 2746:2015 | Vitreous and porcelain enamels — High voltage test |
| ISO 2808:2007 | Paints and varnishes — Determination of film thickness |
| ISO 13806:1999 | Vitreous and porcelain enamels — Corrosion tests in closed systems |
| ISO 3819:2015 | Laboratory glassware — Beakers |