EN ISO 1456:2009

Foreword
Introduction
1 Scope
2 Normative references
3 Terms and definitions
4 Information to be supplied by the purchaser
  to the processor
  4.1 Essential information
  4.2 Additional information
5 Designation
  5.1 General
  5.2 Designation specifications
  5.3 Service-condition number
  5.4 Type of copper coating
  5.5 Types of nickel coating
  5.6 Types and thicknesses of chromium
6 Requirements
  6.1 Appearance
  6.2 Coating thickness
  6.3 Double- and triple-layer nickel coatings
  6.4 Adhesion
  6.5 Corrosion resistance in CASS, Corrodkote and salt
       spray tests
  6.6 STEP test requirements
  6.7 Ductility
  6.8 Stress-relief heat treatments before coating
  6.9 Hydrogen-embrittlement-relief treatment
  6.10 Sampling
Annex A (informative) - Determination of cracks and
                        pores in chromium coatings
Annex B (normative) - Methods of test for the determination
                      of thickness
Annex C (normative) - Ductility test
Annex D (normative) - Determination of the sulfur content
                      of electrodeposited nickel
Annex E (informative) - Step test method
Bibliography

ISO 1456:2009 specifies requirements for decorative nickel, nickel plus chromium, copper plus nickel and copper plus nickel plus chromium coatings that are applied to iron, steel, zinc alloys, copper and copper alloys, and to aluminium and aluminium alloys, to provide an attractive appearance and enhanced corrosion resistance. Coating designations are specified that differ in thickness and type, and guidance is given on selecting the coating designation appropriate for the service conditions to which the coated product will be exposed.ISO 1456:2009 does not specify the surface condition required by the basis metal prior to the coating process, and is not applicable to coatings on sheet, strip or wire in the non-fabricated form nor to threaded fasteners or coil springs.