ISO 10119:2002
Withdrawn
Withdrawn
View Superseded by
Carbon fibre — Determination of density
Available format(s)
Hardcopy , PDF
Language(s)
English, French
Published date
06-13-2002
Withdrawn date
04-09-2025
Superseded by
US$96.00
Excluding Tax where applicable
This International Standard specifies three methods for the determination of the density of carbon fibre yarn:
- method A: liquid-displacement method;
- method B: sink/float method;
- method C: density-gradient column method.
Method C is the reference method.
| Committee |
ISO/TC 61/SC 13
|
| DocumentType |
Standard
|
| Pages |
10
|
| PublisherName |
International Organization for Standardization
|
| Status |
Withdrawn
|
| SupersededBy | |
| Supersedes |
| Standards | Relationship |
| BS ISO 10119:2002 | Identical |
| NBN EN 13003-2 : 1999 | Identical |
| GOST R ISO 10119 : 2012 | Identical |
| NBN EN 2564 : 1998 | Identical |
| NF ISO 10119 : 2003 | Identical |
| IS 17306 : 2019 | Identical |
| BS 7658-1:1993 | Identical |
| NEN ISO 10119 : 2002 | Identical |
| DIN EN 16245-3:2013-08 | FIBRE-REINFORCED PLASTIC COMPOSITES - DECLARATION OF RAW MATERIAL CHARACTERISTICS - PART 3: SPECIFIC REQUIREMENTS FOR FIBRE |
| BS EN 16245-3:2013 | Fibre-reinforced plastic composites. Declaration of raw material characteristics Specific requirements for fibre |
| BS ISO 14127:2008 | Carbon-fibre-reinforced composites. Determination of the resin, fibre and void contents |
| NF EN 16245-3 : 2013 | FIBRE-REINFORCED PLASTIC COMPOSITES - DECLARATION OF RAW MATERIAL CHARACTERISTICS - PART 3: SPECIFIC REQUIREMENTS FOR FIBRE |
| 17/30336191 DC : DRAFT JUL 2017 | BS ISO 11567 - CARBON FIBRE - DETERMINATION OF FILAMENT DIAMETER AND CROSS-SECTIONAL AREA |
| BS ISO 11567:1995 | Carbon fibre. Determination of filament diameter and cross-sectional area |
| BS EN 2564:1998 | Carbon fibre laminates. Determination of the fibre, resin and void contents |
| DD ENV 1007-5:1998 | Advanced technical ceramics. Ceramic composites. Methods of test for reinforcements Determination of distribution of tensile strength and tensile strain to failure of filaments within a multifilament tow at ambient temperature |
| PREN 2564 : DRAFT 2017 | AEROSPACE SERIES - CARBON FIBRE LAMINATES - DETERMINATION OF THE FIBRE, RESIN AND VOID CONTENTS |
| SAE AMS3961/3 | 350 °F Autoclave Cure, Low Flow Toughened Epoxy Prepregs, Type 35, Class 1, Grade 190, Fiber 1 |
| DIN EN 2564:1998-08 | AEROSPACE SERIES - CARBON FIBRE LAMINATES - DETERMINATION OF THE FIBRE-, RESIN- AND VOID CONTENTS |
| DIN EN ISO 10618:2004-11 | Carbon fibre - Determination of tensile properties of resin-impregnated yarn (ISO 10618:2004); German version EN ISO 10618:2004 |
| DIN EN 1007-5:2010-06 | Advanced technical ceramics - Ceramic composites - Methods of test for reinforcements - Part 5: Determination of distribution of tensile strength and of tensile strain to failure of filaments within a multifilament tow at ambient temperature |
| EN 1007-5:2010 | Advanced technical ceramics - Ceramic composites - Methods of test for reinforcements - Part 5: Determination of distribution of tensile strength and of tensile strain to failure of filaments within a multifilament tow at ambient temperature |
| CEN/TS 1007-7:2006 | Advanced technical ceramics - Ceramic composites. Methods of test for reinforcements - Part 7: Determination of the distribution of tensile strength and of tensile strain to failure of filaments within a multifilament tow at high temperature |
| EN 1007-7:2010 | Advanced technical ceramics - Ceramic composites - Methods of test for reinforcements - Part 7: Determination of the distribution of tensile strength and of tensile strain to failure of filaments within a multifilament tow at high temperature |
| EN 13003-3:1999 | Para-aramid fibre filament yarns - Part 3: Technical specifications |
| BS EN 1007-7:2010 | Advanced technical ceramics. Ceramic composites. Methods of test for reinforcements Determination of the distribution of tensile strength and of tensile strain to failure of filaments within a multifilament tow at high temperature |
| SAE AMS3961/1 | 350 °F Autoclave Cure, Low Flow Toughened Epoxy Prepregs, Type 38, Class 2, Grade 193, Style 3K-70-PW, Fiber 1 |
| PREN 6044-2 : 200P1 | AEROSPACE SERIES - CARBON FIBRE REINFORCED EPOXY PREPREG - TECHNICAL SPECIFICATION - QUALIFICATION PROGRAMM/BATCH RELEASE TESTING - UNIDIRECTIONAL TAPE 180 DEGREE C CURING CLASS |
| I.S. EN 1007-7:2010 | ADVANCED TECHNICAL CERAMICS - CERAMIC COMPOSITES - METHODS OF TEST FOR REINFORCEMENTS - PART 7: DETERMINATION OF THE DISTRIBUTION OF TENSILE STRENGTH AND OF TENSILE STRAIN TO FAILURE OF FILAMENTS WITHIN A MULTIFILAMENT TOW AT HIGH TEMPERATURE |
| BS EN ISO 10618:2004 | Carbon fibre. Determination of tensile properties of resin-impregnated yarn |
| I.S. EN ISO 10618:2004 | CARBON FIBRE - DETERMINATION OF TENSILE PROPERTIES OF RESINIMPREGNATED YARN |
| I.S. EN 1007-5:2010 | ADVANCED TECHNICAL CERAMICS - CERAMIC COMPOSITES - METHODS OF TEST FOR REINFORCEMENTS - PART 5: DETERMINATION OF DISTRIBUTION OF TENSILE STRENGTH AND OF TENSILE STRAIN TO FAILURE OF FILAMENTS WITHIN A MULTIFILAMENT TOW AT AMBIENT TEMPERATURE |
| NF EN 1007-5 : 2010 | ADVANCED TECHNICAL CERAMICS - CERAMIC COMPOSITES - METHODS OF TEST FOR REINFORCEMENTS - PART 5: DETERMINATION OF DISTRIBUTION OF TENSILE STRENGTH AND OF TENSILE STRAIN TO FAILURE OF FILAMENTS WITHIN A MULTIFILAMENT TOW AT AMBIENT TEMPERATURE |
| BS ISO 13931:2013 | Carbon fibre. Determination of volume resistivity |
| 08/30183873 DC : DRAFT AUG 2008 | BS EN 1007-5 - ADVANCED TECHNICAL CERAMICS - CERAMIC COMPOSITES - METHODS OF TEST FOR REINFORCEMENTS - PART 5: DETERMINATION OF DISTRIBUTION OF TENSILE STRENGTH AND OF TENSILE STRAIN TO FAILURE OF FILAMENTS WITHIN A MULTIFILAMENT TOW AT AMBIENT TEMPERATURE |
| DIN EN 1007-7:2010-12 | Advanced technical ceramics - Ceramic composites - Methods of test for reinforcements - Part 7: Determination of the distribution of tensile strength and of tensile strain to failure of filaments within a multifilament tow at high temperature |
| PREN 2962 : 200P1 | AEROSPACE SERIES - CARBON FIBRE FILAMENT YARN (POLYACRYLONITRILE PRECURSOR) - TECHNICAL SPECIFICATION |
| NF EN 1007-7 : 2010 | ADVANCED TECHNICAL CERAMICS - CERAMIC COMPOSITES - METHODS OF TEST FOR REINFORCEMENTS - PART 7: DETERMINATION OF THE DISTRIBUTION OF TENSILE STRENGTH AND OF TENSILE STRAIN TO FAILURE OF FILAMENTS WITHIN A MULTIFILAMENT TOW AT HIGH TEMPERATURE |
| ISO 14127:2008 | Carbon-fibre-reinforced composites — Determination of the resin, fibre and void contents |
| EN 2564:1998 | Aerospace series - Carbon fibre laminates - Determination of the fibre, resin and void contents |
| 11/30209308 DC : 0 | BS ISO 13931 - CARBON FIBRE - DETERMINATION OF VOLUME RESISTIVITY |
| NF EN 2564 : 1998 | AEROSPACE SERIES - CARBON FIBRE LAMINATES - DETERMINATION OF THE FIBRE, RESIN AND VOID CONTENTS |
| 09/30210248 DC : 0 | BS EN 1007-7 - ADVANCED TECHNICAL CERAMICS - CERAMIC COMPOSITES - METHODS OF TEST FOR REINFORCEMENTS - PART 7: DETERMINATION OF THE DISTRIBUTION OF TENSILE STRENGTH AND OF TENSILE STRAIN TO FAILURE OF FILAMENTS WITHIN A MULTIFILAMENT TOW AT HIGH TEMPERATURE |
| 16/30346715 DC : 0 | BS EN 2564 - AEROSPACE SERIES - CARBON FIBRE LAMINATES - DETERMINATION OF THE FIBRE, RESIN- AND VOID CONTENTS |
| 11/30239980 DC : DRAFT MAR 2011 | BS EN 16245-3 - FIBRE-REINFORCED PLASTIC COMPOSITES - DECLARATION OF RAW MATERIAL CHARACTERISTICS - PART 3: SPECIFIC REQUIREMENTS FOR FIBRE |
| I.S. EN 16245-3:2013 | FIBRE-REINFORCED PLASTIC COMPOSITES - DECLARATION OF RAW MATERIAL CHARACTERISTICS - PART 3: SPECIFIC REQUIREMENTS FOR FIBRE |
| ISO 13931:2013 | Carbon fibre — Determination of volume resistivity |
| BS EN 13003-1:1999 | Para-aramid fibre filament yarns Designation |
| BS EN 13003-3:1999 | Para-aramid fibre filament yarns Technical specifications |
| BS EN 13003-2:1999 | Para-aramid fibre filament yarns Methods of test and general specifications |
| BS EN 1007-5:2010 | Advanced technical ceramics. Ceramic composites. Methods of test for reinforcements Determination of distribution of tensile strength and of tensile strain to failure of filaments within a multifilament tow at ambient temperature |
| ISO 10618:2004 | Carbon fibre — Determination of tensile properties of resin-impregnated yarn |
| EN ISO 10618:2004 | Carbon fibre - Determination of tensile properties of resin-impregnated yarn (ISO 10618:2004) |
| EN 16245-3:2013 | Fibre-reinforced plastic composites - Declaration of raw material characteristics - Part 3: Specific requirements for fibre |
| ENV 1007-5 : 1998 | ADVANCED TECHNICAL CERAMICS - CERAMIC COMPOSITES - METHODS OF TEST FOR REINFORCEMENTS - DETERMINATION OF DISTRIBUTION OF TENSILE STRENGTH AND OF TENSILE STRAIN TO FAILURE OF FILAMENTS WITHIN A MULTIFILAMENT TOW AT AMBIENT TEMPERATURE |
| ISO 11567:1995 | Carbon fibre — Determination of filament diameter and cross-sectional area |
| SAE AMS3970/1A | Carbon Fiber Fabric Repair Prepreg, 120 °C (250 °F) Vacuum Curing Part 1 - General Requirements |
| I.S. CEN TS 1007-7:2006 | ADVANCED TECHNICAL CERAMICS - CERAMIC COMPOSITES. METHODS OF TEST FOR REINFORCEMENTS - PART 7: DETERMINATION OF THE DISTRIBUTION OF TENSILE STRENGTH AND OF TENSILE STRAIN TO FAILURE OF FILAMENTS WITHIN A MULTIFILAMENT TOW AT HIGH TEMPERATURE |
| BS EN 13002-2:1999 | Carbon fibre yarns Test methods and general specifications |
| EN 13002-2:1999 | Carbon fibre yarns - Part 2: Test methods and general specifications |
| EN 13003-2:1999 | Para-aramid fibre filament yarns - Part 2: Methods of test and general specifications |
| UNE-EN 16245-3:2014 | Fibre-reinforced plastic composites - Declaration of raw material characteristics - Part 3: Specific requirements for fibre |
| ISO 10548:2002 | Carbon fibre — Determination of size content |
| ISO 1675:1985 | Plastics — Liquid resins — Determination of density by the pyknometer method |
| ISO 291:2008 | Plastics — Standard atmospheres for conditioning and testing |
Summarise
US$96.00
Excluding Tax where applicable
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : All end users must be registered with an Account prior to user licenses being assigned.
Users cannot be edited or removed once added to your Multi user PDF.