ISO 3387:2012
Withdrawn
View Superseded by
Rubber — Determination of crystallization effects by hardness measurements
Hardcopy , PDF
English, French
07-02-2012
04-09-2025
ISO 3387:2012 specifies a test based on hardness measurements for determining the progressive stiffening of rubber with time, caused by crystallization. It is limited to materials having an initial hardness at a test temperature of from 10 IRHD to 85 IRHD.
The method is applicable to raw, unvulcanized (compounded) and vulcanized rubber. It is mainly of interest for rubber with a marked crystallization tendency at temperatures experienced in cold climates, such as chloroprene and natural rubber.
The method is not applicable to fast-crystallizing materials which crystallize to a considerable degree within the time-span of 15 min used for conditioning at test temperature.
| Committee |
ISO/TC 45/SC 2
|
| DevelopmentNote |
Supersedes ISO/DIS 3387. (07/2012)
|
| DocumentType |
Standard
|
| Pages |
10
|
| PublisherName |
International Organization for Standardization
|
| Status |
Withdrawn
|
| SupersededBy | |
| Supersedes |
| Standards | Relationship |
| NF ISO 3387 : 2012 | Identical |
| BS ISO 3387:2012 | Identical |
| NEN ISO 3387 : 2012 | Identical |
| UNE 53631:2003 | Identical |
| UNE-ISO 3387:2013 | Identical |
| DIN EN ISO 3887:2016-08 (Draft) | Corresponds |
| DIN 53541:1980-01 | Corresponds |
| NBN ISO 3387 : 2003 | Identical |
| NBN T 31 034 : 1980 | Identical |
| DIN EN ISO 3887:2003-10 | Corresponds |
A newer version of this standard is available.
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : All end users must be registered with an Account prior to user licenses being assigned.
Users cannot be edited or removed once added to your Multi user PDF.