Implants for surgery — Ceramic materials — Part 1: Ceramic materials based on high purity alumina
Available format(s)
Hardcopy , PDF
Language(s)
English, French, Russian
Published date
01-28-2010
Withdrawn date
04-09-2025
Superseded by
US$96.00
Excluding Tax where applicable
ISO 6474-1:2010 specifies the characteristics of, and corresponding test methods for, a bio-compatible and bio-stable ceramic bone substitute material based on high purity alumina for use as bone spacers, bone replacements and components of orthopaedic joint prostheses.
| Committee |
ISO/TC 150/SC 1
|
| DevelopmentNote |
Supersedes ISO 6474. (02/2012) DRAFT ISO/DIS 6474-1 is also available for this standard. (04/2016)
|
| DocumentType |
Standard
|
| Pages |
9
|
| PublisherName |
International Organization for Standardization
|
| Status |
Withdrawn
|
| SupersededBy | |
| Supersedes |
| Standards | Relationship |
| NF ISO 6474-1 : 2010 | Identical |
| BS ISO 6474-1:2010 | Identical |
| GOST R ISO 6474-1 : 2014 | Identical |
| I.S. EN ISO 10555-6:2017 | INTRAVASCULAR CATHETERS - STERILE AND SINGLE-USE CATHETERS - PART 6: SUBCUTANEOUS IMPLANTED PORTS (ISO 10555-6:2015) |
| DIN EN ISO 10555-6:2017-11 | INTRAVASCULAR CATHETERS - STERILE AND SINGLE-USE CATHETERS - PART 6: SUBCUTANEOUS IMPLANTED PORTS (ISO 10555-6:2015) |
| 13/30261812 DC : 0 | BS ISO 10555-6 - INTRAVASCULAR CATHETERS - STERILE AND SINGLE-USE CATHETERS - PART 6: SUBCUTANEOUS IMPLANTED PORTS |
| BS ISO 6474-2:2012 | Implants for surgery. Ceramic materials Composite materials based on a high-purity alumina matrix with zirconia reinforcement |
| BS ISO 12891-2:2014 | Retrieval and analysis of surgical implants Analysis of retrieved surgical implants |
| ANSI/AAMI/ISO 16142-1:2016 | MEDICAL DEVICES - RECOGNIZED ESSENTIAL PRINCIPLES OF SAFETY AND PERFORMANCE OF MEDICAL DEVICES - PART 1: GENERAL ESSENTIAL PRINCIPLES AND ADDITIONAL SPECIFIC ESSENTIAL PRINCIPLES FOR ALL NON-IVD MEDICAL DEVICES AND GUIDANCE ON THE SELECTION OF STANDARDS |
| BS EN ISO 10993-6:2016 | Biological evaluation of medical devices Tests for local effects after implantation |
| I.S. EN ISO 10993-6:2016 | BIOLOGICAL EVALUATION OF MEDICAL DEVICES - PART 6: TESTS FOR LOCAL EFFECTS AFTER IMPLANTATION (ISO 10993-6:2016) |
| I.S. EN ISO 10451:2010 | DENTISTRY - CONTENTS OF TECHNICAL FILE FOR DENTAL IMPLANT SYSTEMS |
| BS ISO 10555-6 : 2015 | INTRAVASCULAR CATHETERS - STERILE AND SINGLE-USE CATHETERS - PART 6: SUBCUTANEOUS IMPLANTED PORTS |
| EN ISO 10555-6:2017 | Intravascular catheters - Sterile and single-use catheters - Part 6: Subcutaneous implanted ports (ISO 10555-6:2015) |
| 10/30196848 DC : 0 | BS ISO 6474-2 - IMPLANTS FOR SURGERY - CERAMIC MATERIALS - PART 2: COMPOSITE MATERIALS BASED ON A HIGH PURITY ALUMINA MATRIX WITH ZIRCONIA REINFORCEMENT |
| BS ISO 16142-1:2016 | Medical devices. Recognized essential principles of safety and performance of medical devices General essential principles and additional specific essential principles for all non-IVD medical devices and guidance on the selection of standards |
| ANSI/AAMI/ISO 10993-6:2016 | BIOLOGICAL EVALUATION OF MEDICAL DEVICES - PART 6: TESTS FOR LOCAL EFFECTS AFTER IMPLANTATION |
| ISO 16142-1:2016 | Medical devices — Recognized essential principles of safety and performance of medical devices — Part 1: General essential principles and additional specific essential principles for all non-IVD medical devices and guidance on the selection of standards |
| ASTM F 3018 : 2017 | Standard Guide for Assessment of Hard-on-Hard Articulation Total Hip Replacement and Hip Resurfacing Arthroplasty Devices |
| BS EN ISO 10555-6:2017 | Intravascular catheters. Sterile and single-use catheters Subcutaneous implanted ports |
| ISO 6474-2:2012 | Implants for surgery — Ceramic materials — Part 2: Composite materials based on a high-purity alumina matrix with zirconia reinforcement |
| ISO 10555-6:2015 | Intravascular catheters — Sterile and single-use catheters — Part 6: Subcutaneous implanted ports |
| 17/30361518 DC : 0 | BS ISO 6474-2 - IMPLANTS FOR SURGERY - CERAMIC MATERIALS - PART 2: COMPOSITE MATERIALS BASED ON A HIGH-PURITY ALUMINA MATRIX WITH ZIRCONIA REINFORCEMENT |
| 14/30261590 DC : 0 | BS EN ISO 10993-6 - BIOLOGICAL EVALUATION OF MEDICAL DEVICES - PART 6: TESTS FOR LOCAL EFFECTS AFTER IMPLANTATION |
| 13/30242622 DC : 0 | BS ISO 12891-2 - RETRIEVAL AND ANALYSIS OF SURGICAL IMPLANTS - PART 2: ANALYSIS OF RETRIEVED SURGICAL IMPLANTS |
| ISO 12891-2:2014 | Retrieval and analysis of surgical implants — Part 2: Analysis of retrieved surgical implants |
| BS EN ISO 10451:2010 | Dentistry. Contents of technical file for dental implant systems |
| ISO 10451:2010 | Dentistry — Contents of technical file for dental implant systems |
| EN ISO 10993-6:2016 | Biological evaluation of medical devices - Part 6: Tests for local effects after implantation (ISO 10993-6:2016) |
| EN ISO 10451:2010 | Dentistry - Contents of technical file for dental implant systems (ISO 10451:2010) |
| ASTM F 2091 : 2015 : REDLINE | Standard Specification for Acetabular Prostheses |
| ASTM F 2083 : 2012 : REDLINE | Standard Specification for Knee Replacement Prosthesis |
| DIN EN ISO 10451:2010-11 | Dentistry - Contents of technical file for dental implant systems (ISO 10451:2010) |
| DIN EN ISO 10993-6:2009-08 | BIOLOGICAL EVALUATION OF MEDICAL DEVICES - PART 6: TESTS FOR LOCAL EFFECTS AFTER IMPLANTATION (ISO 10993-6:2016) |
| ISO 10993-6:2016 | Biological evaluation of medical devices — Part 6: Tests for local effects after implantation |
| DIN EN ISO 10993-6:2017-09 | BIOLOGICAL EVALUATION OF MEDICAL DEVICES - PART 6: TESTS FOR LOCAL EFFECTS AFTER IMPLANTATION (ISO 10993-6:2016) |
| ISO 23146:2012 | Fine ceramics (advanced ceramics, advanced technical ceramics) — Test methods for fracture toughness of monolithic ceramics — Single-edge V-notch beam (SEVNB) method |
| EN 843-2:2006 | Advanced technical ceramics - Mechanical properties of monolithic ceramics at room temperature - Part 2: Determination of Young's modulus, shear modulus and Poisson's ratio |
| ISO 20501:2003 | Fine ceramics (advanced ceramics, advanced technical ceramics) — Weibull statistics for strength data |
| EN 843-1:2006 | Advanced technical ceramics - Mechanical properties of monolithic ceramics at room temperature - Part 1: Determination of flexural strength |
| ISO 18754:2013 | Fine ceramics (advanced ceramics, advanced technical ceramics) — Determination of density and apparent porosity |
| ISO 14242-1:2014 | Implants for surgery — Wear of total hip-joint prostheses — Part 1: Loading and displacement parameters for wear-testing machines and corresponding environmental conditions for test |
| ISO 12677:2011 | Chemical analysis of refractory products by X-ray fluorescence (XRF) — Fused cast-bead method |
| EN 843-5:2006 | Advanced technical ceramics - Mechanical properties of monolithic ceramics at room temperature - Part 5: Statistical analysis |
| ASTM C 1327 : 2015 : REDLINE | TEST METHOD FOR VICKERS INDENTATION HARDNESS OF ADVANCED CERAMICS |
| ISO 10993-14:2001 | Biological evaluation of medical devices — Part 14: Identification and quantification of degradation products from ceramics |
| ISO 13356:2015 | Implants for surgery — Ceramic materials based on yttria-stabilized tetragonal zirconia (Y-TZP) |
| EN 725-1:2007 | Advanced technical ceramics - Methods of test for ceramic powders - Part 1: Determination of impurities in alumina |
| ISO 22214:2006 | Fine ceramics (advanced ceramics, advanced technical ceramics) — Test method for cyclic bending fatigue of monolithic ceramics at room temperature |
| ASTM C 1259 : 2015 : REDLINE | Standard Test Method for Dynamic Young’s Modulus, Shear Modulus, and Poisson’s Ratio for Advanced Ceramics by Impulse Excitation of Vibration |
| ISO 14705:2016 | Fine ceramics (advanced ceramics, advanced technical ceramics) — Test method for hardness of monolithic ceramics at room temperature |
| EN 623-2:1993 | Advanced technical ceramics - Monolithic ceramics - General and textural properties - Part 2: Determination of density and porosity |
| ISO 14704:2016 | Fine ceramics (advanced ceramics, advanced technical ceramics) — Test method for flexural strength of monolithic ceramics at room temperature |
| ISO 18756:2003 | Fine ceramics (advanced ceramics, advanced technical ceramics) — Determination of fracture toughness of monolithic ceramics at room temperature by the surface crack in flexure (SCF) method |
| CEN/TS 14425-5 : 2004 | ADVANCED TECHNICAL CERAMICS - TEST METHODS FOR DETERMINATION OF FRACTURE TOUGHNESS OF MONOLITIC CERAMICS - PART 5: SINGLE-EDGE VEE-NOTCH BEAM (SEVNB) METHOD |
| EN 843-4:2005 | Advanced technical ceramics - Mechanical properties of monolithic ceramics at room temperature - Part 4: Vickers, Knoop and Rockwell superficial hardness |
| EN 623-3:2001 | Advanced technical ceramics - Monolithic ceramics - General and textural properties - Part 3: Determination of grain size and size distribution (characterized by the Linear Intercept Method) |
| ASTM C 1499 : 2015 : REDLINE | TEST METHOD FOR MONOTONIC EQUIBIAXIAL FLEXURAL STRENGTH OF ADVANCED CERAMICS AT AMBIENT TEMPERATURE |
| ISO 10993-9:2009 | Biological evaluation of medical devices — Part 9: Framework for identification and quantification of potential degradation products |
| ISO 17561:2016 | Fine ceramics (advanced ceramics, advanced technical ceramics) — Test method for elastic moduli of monolithic ceramics at room temperature by sonic resonance |
| ISO 15732:2003 | Fine ceramics (advanced ceramics, advanced technical ceramics) — Test method for fracture toughness of monolithic ceramics at room temperature by single edge precracked beam (SEPB) method |
Summarise
US$96.00
Excluding Tax where applicable
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : All end users must be registered with an Account prior to user licenses being assigned.
Users cannot be edited or removed once added to your Multi user PDF.