MIL-STD-1877 Revision B:1990
Withdrawn
BRAZING, NICKEL, HIGH TEMPERATURE VACUUM (METRIC) (NO S/S DOCUMENT)
English
12-12-1990
02-17-1993
Specifies requirements for brazing in a vacuum atmosphere furnace utilising nickel base brazing alloys
| DocumentType |
Standard
|
| Pages |
21
|
| PublisherName |
US Military Specs/Standards/Handbooks
|
| Status |
Withdrawn
|
This standard covers the requirements for brazing in a vacuum atmosphere furnace using nickel base brazing alloys.
| MIL-H-6875 Revision H:1989 | Heat Treatment of Steel, Process for (S/S by SAE-AMS-H-6875) |
| SAE AMS4777H | Nickel Alloy, Brazing Filler Metal 82Ni - 4.5Si - 7.0Cr - 3.1B - 3.0Fe 1780 to 1830 °F (971 to 999 °C) Solidus-Liquidus Range |
| SAE AMS4779J | Nickel Alloy, Brazing Filler Metal 94Ni - 3.5Si - 1.8B 1800 °F (982 °C) Solidus, 1950 °F (1066 °C) Liquidus |
| SAE AMS5510S | Steel, Corrosion and Heat-Resistant, Sheet, Strip and Plate 18Cr - 10.5Ni - 0.40Ti (SAE 30321) Solution Heat Treated |
| MIL-STD-865 Revision D:2007 | Selective Brush Plating, Electro-Deposition |
| SAE AMS4776H | Nickel Alloy, Brazing Filler Metal 73Ni - 4.5Si - 14Cr - 3.1B - 4.5Fe (Low Carbon) 1790 to 1970 °F (977 to 1077 °C) Solidus-Liquidus Range |
| MIL-T-81533 Revision A:1967 | Trichloroethane 1, 1, 1, (Methyl Chloroform) Inhibited, Vapor Degreasing (No S/S Document) |
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : All end users must be registered with an Account prior to user licenses being assigned.
Users cannot be edited or removed once added to your Multi user PDF.