EN ISO 4628-8:2012
Current
Current
The latest, up-to-date edition.
Paints and varnishes - Evaluation of degradation of coatings - Designation of quantity and size of defects, and of intensity of uniform changes in appearance - Part 8: Assessment of degree of delamination and corrosion around a scribe or other artificial defect (ISO 4628-8:2012)
Published date
01-11-2012
Publisher
Sorry this product is not available in your region.
Foreword
Introduction
1 Scope
2 Normative references
3 Terms and definitions
4 Principle
5 Procedure
6 Calculation and expression of results
7 Test report
Bibliography
ISO 4628-8:2012 specifies a method for assessing delamination and corrosion around a scribe or other artificial defect on a coated panel or other coated test specimen, caused by a corrosive environment.ISO 4628-8:2012 does not cover evaluation of pitting corrosion or pit depth.
| Committee |
CEN/TC 139
|
| DocumentType |
Standard
|
| PublisherName |
Comite Europeen de Normalisation
|
| Status |
Current
|
| Standards | Relationship |
| NEN EN ISO 4628-8 : 2012 | Identical |
| NF EN ISO 4628-8 : 2013 | Identical |
| I.S. EN ISO 4628-8:2012 | Identical |
| BS EN ISO 4628-8:2012 | Identical |
| NBN EN ISO 4628-8 : 2013 | Identical |
| ISO 4628-8:2012 | Identical |
| NS EN ISO 4628-8 : 2012 | Identical |
| DIN EN ISO 4628-8:2013-03 | Identical |
| PN EN ISO 4628-8 : 2013 | Identical |
| SS-EN ISO 4628-8:2012 | Identical |
| BS 3900-H8(2005) : 2005 | Identical |
| UNE-EN ISO 4628-8:2013 | Identical |
| 17/30371343 DC : 0 | BS EN 4688 - AEROSPACE SERIES - PAINTS AND VARNISHES - CORROSION RESISTANT CHROMATED TWO COMPONENT COLD CURING EPOXY PRIMER - HIGH CORROSION RESISTANCE FOR MILITARY APPLICATION |
| 17/30371344 DC : 0 | BS EN 4689 - AEROSPACE SERIES - PAINTS AND VARNISHES - TWO COMPONENTS COLD CURING POLYURETHANE FINISH - HIGH FLEXIBILITY AND CHEMICAL AGENT RESISTANCE FOR MILITARY APPLICATION |
| 12/30268970 DC : 0 | BS EN 13523-25 - COIL COATED METALS - TEST METHODS - PART 25: RESISTANCE TO HUMIDITY |
| PREN 4689 : 200P1 | AEROSPACE SERIES - PAINTS AND VARNISHES - TWO COMPONENTS COLD CURING POLYURETHANE FINISH - HIGH FLEXIBILITY AND CHEMICAL AGENT RESISTANCE FOR MILITARY APPLICATION |
| BS EN 13523-8:2017 | Coil coated metals. Test methods Resistance to salt spray (fog) |
| EN 13523-9:2014 | Coil coated metals - Test methods - Part 9: Resistance to water immersion |
| EN 13523-8:2017 | Coil coated metals - Test methods - Part 8: Resistance to salt spray (fog) |
| PREN 13523-21 : DRAFT 2016 | COIL COATED METALS - TEST METHODS - PART 21: EVALUATION OF OUTDOOR EXPOSED PANELS |
| BS EN 4689:2012 | Aerospace series. Paints and varnishes. Two components cold curing polyurethane finish. High flexibility and chemical agent resistance for military application |
| PREN 13523-8 : DRAFT 2016 | COIL COATED METALS - TEST METHODS - PART 8: RESISTANCE TO SALT SPRAY (FOG) |
| I.S. EN 13523-25:2014 | COIL COATED METALS - TEST METHODS - PART 25: RESISTANCE TO HUMIDITY |
| I.S. EN 13523-21:2017 | COIL COATED METALS - TEST METHODS - PART 21: EVALUATION OF OUTDOOR EXPOSED PANELS |
| I.S. EN 13523-8:2017 | COIL COATED METALS - TEST METHODS - PART 8: RESISTANCE TO SALT SPRAY (FOG) |
| EN 4689:2012 | Aerospace series - Paints and varnishes - Two components cold curing polyurethane finish - High flexibility and chemical agent resistance for military application |
| EN 4688:2012 | Aerospace series - Paints and varnishes - Corrosion inhibiting two components cold curing primer for military application |
| I.S. EN 13523-9:2014 | COIL COATED METALS - TEST METHODS - PART 9: RESISTANCE TO WATER IMMERSION |
| 16/30340560 DC : 0 | BS EN 13523-8 - COIL COATED METALS - TEST METHODS - PART 8: RESISTANCE TO SALT SPRAY (FOG) |
| 12/30268964 DC : 0 | BS EN 13523-9 - COIL COATED METALS - TEST METHODS - PART 9: RESISTANCE TO WATER IMMERSION |
| DIN EN 13523-21:2016-07 (Draft) | COIL COATED METALS - TEST METHODS - PART 21: EVALUATION OF OUTDOOR EXPOSED PANELS |
| I.S. EN 4689:2012 | AEROSPACE SERIES - PAINTS AND VARNISHES - TWO COMPONENTS COLD CURING POLYURETHANE FINISH - HIGH FLEXIBILITY AND CHEMICAL AGENT RESISTANCE FOR MILITARY APPLICATION |
| PREN 4688 : 200P1 | AEROSPACE SERIES - PAINTS AND VARNISHES - CORROSION INHIBITING TWO COMPONENTS COLD CURING PRIMER FOR MILITARY APPLICATION |
| I.S. EN 4688:2012 | AEROSPACE SERIES - PAINTS AND VARNISHES - CORROSION INHIBITING TWO COMPONENTS COLD CURING PRIMER FOR MILITARY APPLICATION |
| PREN 13523-9 : DRAFT 2012 | COIL COATED METALS - TEST METHODS - PART 9: RESISTANCE TO WATER IMMERSION |
| DIN EN 13523-25:2014-08 | Coil coated metals - Test methods - Part 25: Resistance to humidity |
| DIN EN 13523-9:2014-08 | Coil coated metals - Test methods - Part 9: Resistance to water immersion |
| BS EN 13523-25:2014 | Coil coated metals. Test methods Resistance to humidity |
| BS EN 13523-21:2017 | Coil coated metals. Test methods Evaluation of outdoor exposed panels |
| EN 13523-21:2017 | Coil coated metals - Test methods - Part 21: Evaluation of outdoor exposed panels |
| DIN EN 13523-8:2016-07 (Draft) | COIL COATED METALS - TEST METHODS - PART 8: RESISTANCE TO SALT SPRAY (FOG) |
| BS EN 4688:2012 | Aerospace series. Paints and varnishes. Corrosion inhibiting two components cold curing primer for military application |
| 16/30340557 DC : 0 | BS EN 13523-21 - COIL COATED METALS - TEST METHODS - PART 21: EVALUATION OF OUTDOOR EXPOSED PANELS |
| PREN 4868 : DRAFT 2018 | AEROSPACE SERIES - ANODIC ELECTRODEPOSITION OF HEXAVALENT CHROMIUM FREE PRIMER |
| BS EN 13523-9:2014 | Coil coated metals. Test methods Resistance to water immersion |
| EN 13523-25:2014 | Coil coated metals - Test methods - Part 25: Resistance to humidity |
| UNE-EN 13523-25:2014 | Coil coated metals - Test methods - Part 25: Resistance to humidity |
| UNE-EN 13523-9:2014 | Coil coated metals - Test methods - Part 9: Resistance to water immersion |
| UNE-EN 13523-8:2017 | Coil coated metals - Test methods - Part 8: Resistance to salt spray (fog) |
| UNE-EN 13523-21:2017 | Coil coated metals - Test methods - Part 21: Evaluation of outdoor exposed panels |
| ISO 15711:2003 | Paints and varnishes — Determination of resistance to cathodic disbonding of coatings exposed to sea water |
| ISO 4628-4:2016 | Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 4: Assessment of degree of cracking |
| ISO 4628-3:2016 | Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 3: Assessment of degree of rusting |
| ISO 4628-10:2016 | Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 10: Assessment of degree of filiform corrosion |
| ISO 4628-5:2016 | Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 5: Assessment of degree of flaking |
| ISO 4628-1:2016 | Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 1: General introduction and designation system |
| ISO 9227:2017 | Corrosion tests in artificial atmospheres — Salt spray tests |
| ISO 3270:1984 | Paints and varnishes and their raw materials — Temperatures and humidities for conditioning and testing |
| ISO 4628-2:2016 | Paints and varnishes — Evaluation of degradation of coatings — Designation of quantity and size of defects, and of intensity of uniform changes in appearance — Part 2: Assessment of degree of blistering |
Summarise
Sorry this product is not available in your region.