AEROSPACE SERIES - HEAT RESISTING ALLOY NI-PH1302 (NICR20CO13MO4TI3AL) - SOLUTION TREATED AND COLD WORKED - BAR FOR FORGED FASTENERS - 3 MM <= D <= 30 MM
Hardcopy , PDF
English
31-10-1999
0 Introduction
1 Scope
2 Normative references
Specifies the requirements relating to: Heat resisting alloy NI-PH1302 (NiCr20Co13Mo4Ti3Al) - Solution treated and cold worked - Bar for forged fasteners - 3 mm <= D <= 30 mm for aerospace applications.
Committee |
C5
|
DocumentType |
Draft
|
Pages |
6
|
PublisherName |
Aerospace & Defence Industries Association of Europe
|
Status |
Current
|
Standards | Relationship |
DIN EN 2959:2000-03 (Draft) | Identical |
I.S. EN 3294:2008 | AEROSPACE SERIES - BOLTS, T-HEAD, CLOSE TOLERANCE, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), UNCOATED FOR INCREASED HEIGHT NUTS - CLASSIFICATION: 1210 MPA/730 DEGREES C |
XP PREN 4120 : 1994 XP | AEROSPACE SERIES - NUTS, BIHEXAGONAL, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED ON THREAD - CLASSIFICATION: 1 210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
PREN 2582 : 200P1 | AEROSPACE SERIES - BOLTS IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY) - CLASSIFICATION: 1210 MPA/730 DEGREES C - TECHNICAL SPECIFICATION |
PREN 3389 : 200P1 | AEROSPACE SERIES - FASTENERS, EXTERNALLY THREADED, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY) - CLASSIFICATION: 1210 MPA/730 DEGREES C - MANUFACTURING METHOD OPTIONAL - TECHNICAL SPECIFICATION |
NF EN 4124 : 2005 | AEROSPACE SERIES - SHANK NUTS, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-PH1302 (WASPALOY), SILVER PLATED ON THREAD, FOR 60 DEGREES SWAGE - CLASSIFICATION: 1 210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREES C |
PREN 4624 : 200P1 | AEROSPACE SERIES - INSERTS, MJ THREADS, SELF-LOCKING, WITH SELF-BROACHING KEYS, IN HEAT RESISTING NICKEL BASE ALLOY NI-PH1302 (WASPALOY), SILVER PLATED |
PREN 4120 : 200P1 | AEROSPACE SERIES - NUTS, BIHEXAGONAL, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED ON THREAD - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
I.S. EN 4624:2010 | AEROSPACE SERIES - INSERTS, MJ THREADS, SELF-LOCKING, WITH SELF-BROACHING KEYS, IN HEAT RESISTING NICKEL BASE ALLOY NI-PH1302 (WASPALOY), SILVER PLATE |
I.S. EN 4673-005:2010 | AEROSPACE SERIES - INSERTS, UNJ THREADS, SELF-LOCKING, WITH SELF-BROACHING KEYS - PART 005: IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATING |
EN 2930 : 1996 | BOLTS, DOUBLE HEXAGON HEAD, RELIEVED SHANK, LONG THREAD, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
DIN EN 3379:1996-05 | AEROSPACE SERIES - BOLTS, DOUBLE HEXAGON HEAD, CLOSE TOLERANCE SHANK, MEDIUM LENGTH THREAD, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), FOR INCREASED HEIGHT NUTS - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREES C |
BS EN 3672:2016 | Aerospace series. Shank nuts, self-locking, in heat resisting nickel base alloy NI-P101HT (Waspaloy), silver plated, for 30°C swage. Classification. 1 210 MPa (at ambient temperature) / 730°C |
XP PREN 2935 : 1993 XP | AEROSPACE SERIES - BOLTS T-HEAD, RELIEVED SHANK, LONG THREAD, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY) UNPLATED - CLASSIFICATION: 1210 MPA/730 DEGREE C |
PREN 4632-005 : 200P1 | AEROSPACE SERIES - WELDABILITY AND BRAZEABILITY OF MATERIALS IN AEROSPACE CONSTRUCTIONS - PART 005: WELDING AND BRAZING OF HOMOGENOUS ASSEMBLIES OF HEAT RESISTING NI OR CO BASE ALLOYS |
PREN 3294 : 200P1 | AEROSPACE SERIES - BOLTS, T-HEAD, CLOSE TOLERANCE IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), UNCOATED FOR INCREASED HEIGHT NUTS - CLASSIFICATION: 1210 MPA/730 DEGREES C |
I.S. EN 3672:2016 | AEROSPACE SERIES - SHANK NUTS, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED, FOR 30 DEGREE C SWAGE - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
DIN EN 2935:1996-05 | AEROSPACE SERIES - BOLTS, T-HEAD, RELIEVED SHANK, LONG THREAD, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY) - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
DIN EN 2936:1996-05 | AEROSPACE SERIES - BOLTS, T-HEAD, RELIEVED SHANK, LONG THREAD, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED - CLASSIFICATION 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
DIN EN 3010:1998-07 | AEROSPACE SERIES - BOLTS, HEXAGON HEAD, RELIEVED SHANK, LONG THREAD, IN RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY) - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREES C |
DIN EN 3013:1995-11 | AEROSPACE SERIES - NUTS, BIHEXAGONAL, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREES C |
DIN EN 2930:1996-04 | AEROSPACE SERIES - BOLTS, DOUBLE HEXAGON HEAD, RELIEVED SHANK, LONG THREAD, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
DIN EN 3011:1998-07 | AEROSPACE SERIES - BOLTS, HEXAGON HEAD, RELIEVED SHANK, LONG THREAD, IN RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVERPLATED - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREES C |
BS EN 3389:2009 | Aerospace series. Fasteners, externally threaded, in heat resisting nickel base alloy NI-PH1302 (Waspaloy). Classification: 1210 MPa/730°C. Manufacturing method optional. Technical specification |
XP PREN 2930 : 1993 XP | AEROSPACE SERIES - BOLTS WITH DOUBLE HEXAGON HEAD, RELIEVED SHANK, LONG THREAD, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED - CLASSIFICATION: 1 210 MPA/735 DEGREE C |
I.S. EN 4124:2005 | AEROSPACE SERIES - SHANK NUTS, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-PH1302 (WASPALOY), SILVER PLATED ON THREAD, FOR 60 DEGREE SWAGE - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE CELSIUS |
DIN EN 2929:1996-04 | AEROSPACE SERIES - BOLTS, DOUBLE HEXAGON HEAD, RELIEVED SHANK, LONG THREAD, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY) - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
14/30314132 DC : 0 | BS EN 3672 - AEROSPACE SERIES - SHANK NUTS, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED, FOR 30 DEGREE SWAGE - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
BS EN 3637:2008 | Aerospace series. Nuts, self-locking, bihexagonal (double reduced), in heat resisting nickel base alloy NI-P101HT (Waspaloy), silver plated, Classification: 1210 MPa/730 °C |
BS EN 3294:2008 | Aerospace series. Bolts, T-head, close tolerance, in heat resisting nickel base alloy NI-P101HT (Waspaloy), uncoated for increased height nuts. Classification: 1210 MPa/730°C |
EN 2935 : 1996 | AEROSPACE SERIES - BOLTS, T-HEAD, RELIEVED SHANK, LONG THREAD, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY) - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
EN 3239 : 1995 | AEROSPACE SERIES - NUTS, BIHEXAGONAL, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED THREAD - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
UNI EN 4673-005 : 2011 | AEROSPACE SERIES - INSERTS, UNJ THREADS, SELF-LOCKING, WITH SELF- BROACHING KEYS - PART 005: IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATING |
UNI EN 4624 : 2011 | AEROSPACE SERIES - INSERTS, MJ THREADS, SELF-LOCKING, WITH SELF-BROACHING KEYS, IN HEAT RESISTING NICKEL BASE ALLOY NI-PH1302 (WASPALOY), SILVER PLATE |
I.S. EN 3389:2009 | AEROSPACE SERIES - FASTENERS, EXTERNALLY THREADED, IN HEAT RESISTING NICKEL BASE ALLOY NI-PH1302 (WASPALOY) - CLASSIFICATION: 1210 MPA/730 DEGREE C - MANUFACTURING METHOD OPTIONAL - TECHNICAL SPECIFICATION |
XP PREN 4124 : 1994 XP | AEROSPACE SERIES - SHANK NUTS, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED ON THREAD, FOR 60 DEGREE SWAGE - CLASSIFICATION: 1 210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
PREN 3005 : 200P1 | AEROSPACE SERIES - NUTS, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY) - CLASSIFICATION: 1210 MPA/730 DEGREES C - TECHNICAL SPECIFICATION |
XP PREN 2929 : 1993 XP | AEROSPACE SERIES - BOLTS WITH DOUBLE HEXAGON HEAD, RELIEVED SHANK, LONG THREAD, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY) - CLASSIFICATION: 1 210 MPA/735 DEGREE C |
XP PREN 2936 : 1993 XP | AEROSPACE SERIES - BOLTS T-HEAD, RELIEVED SHANK, LONG THREAD, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY) SILVER PLATED - CLASSIFICATION: 1210 MPA/730 DEGREE C |
PREN 4124 : 200P1 | AEROSPACE SERIES - SHANK NUTS, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-PH1302 (WASPALOY), SILVER PLATED ON THREAD, FOR 60 DEGREES SWAGE - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREES C |
I.S. EN 3637:2008 | AEROSPACE SERIES - NUTS, SELF-LOCKING, BI-HEXAGONAL (DOUBLE REDUCED), IN HEAT RESISTING NICKEL BASE ALLOY - NI-P101HT (WASPALOY), SILVER PLATED, CLASSIFICATION: 1210 MPA/730 DEGREE C |
I.S. EN 4632-005:2009 | AEROSPACE SERIES - WELDABILITY AND BRAZEABILITY OF MATERIALS IN AEROSPACE CONSTRUCTIONS - PART 005: HOMOGENEOUS ASSEMBLIES OF HEAT RESISTING NI OR CO BASE ALLOYS |
DIN EN 3012:1995-11 | AEROSPACE SERIES - NUTS, BIHEXAGONAL, SELF-LOCKING, IN RESISTING NICKEL BASSE ALLOY NI-9101HT (WASPALOY) - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREES C |
BS EN 2929:1996 | Bolts, double hexagon head, relieved shank, long thread, in heat resisting nickel base alloy NI-P101HT (Waspaloy). Classification: 1210 MPa (at ambient temperature)/730°C |
17/30369678 DC : 0 | PREN 7010 - AEROSPACE SERIES - USER GUIDE FOR CREATION AND DESIGNATION OF BOLTS |
BS EN 4632-005:2009 | Aerospace series. Weldability and brazeability of materials in aerospace constructions Homogeneous assemblies of heat resisting Ni or Co base alloys |
BS EN 3239:1996 | Nuts, bihexagonal, self-locking, in heat resisting nickel base alloy NI-P101HT (Waspaloy), silver plated thread. Classification: 1210 MPa (at ambient temperature)/730°C |
08/30185224 DC : DRAFT JULY 2008 | BS EN 4673-004 - AEROSPACE SERIES - INSERTS, UNJ THREADS, SELF-LOCKING, WITH SELF-BROACHING KEYS - PART 004: IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATING |
EN 3637:2008 | Aerospace series - Nuts, self-locking, bi-hexagonal (double reduced), in heat resisting nickel base alloy - NI-P101HT (Waspaloy), silver plated, Classification: 1210 MPa/730 °C |
EN 2929 : 1996 | Aerospace series - Bolts, double hexagon head, relieved shank, long thread, in heat resisting nickel base alloy NI-P101HT (Waspaloy) - Classification: 1 210 MPa (at ambient temperature)/730 °C |
EN 3294 : 2008 | Aerospace series - Bolts, T-head, close tolerance, in heat resisting nickel base alloy NI-P101HT (Waspaloy), uncoated for increased height nuts -Classification: 1 210 MPa/730 °C |
EN 4632-005:2009 | Aerospace series - Weldability and brazeability of materials in aerospace constructions - Part 005: Homogeneous assemblies of heat resisting Ni or Co base alloys |
EN 3012 : 1995 | AEROSPACE SERIES - NUTS, BIHEXAGONAL, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY) - CLASSIFICATION 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
EN 4624:2010 | Aerospace series - Inserts, MJ threads, self-locking, with self-broaching keys, in heat resisting nickel base alloy NI-PH1302 (Waspaloy), silver plate |
EN 4673-005:2010 | Aerospace series - Inserts, UNJ threads, self-locking, with self-broaching keys - Part 005: In heat resisting nickel base alloy NI-P101HT (WASPALOY), silver plating |
EN 3013 : 1995 | AEROSPACE SERIES - NUTS, BIHEXAGONAL, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED - CLASSIFICATION 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
EN 2936 : 1996 | AEROSPACE SERIES - BOLTS, T-HEAD, RELIEVED SHANK, LONG THREAD, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
EN 3379:1996 | Aerospace series - Bolts, double hexagon head, close tolerance shank, medium length thread, in heat resisting nickel base alloy NI-P101HT (Waspaloy), for increased height nuts - Classification: 1 210 MPa (at ambient temperature)/730°C |
EN 3672:2016 | Aerospace series - Shank nuts, self-locking, in heat resisting nickel base alloy NI-P101HT (Waspaloy), silver plated, for 30° swage - Classification: 1 210 MPa (at ambient temperature) / 730 °C |
EN 3389 : 2009 | AEROSPACE SERIES - FASTENERS, EXTERNALLY THREADED, IN HEAT RESISTING NICKEL BASE ALLOY NI-PH1302 (WASPALOY) - CLASSIFICATION: 1210 MPA/730 DEGREE C - MANUFACTURING METHOD OPTIONAL - TECHNICAL SPECIFICATION |
XP PREN 3672 : 1994 XP | AEROSPACE SERIES - SHANK NUTS, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED, FOR 30 DEGREE SWAGE - CLASSIFICATION: 1 210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREE C |
PREN 3672 : 200P2 | AEROSPACE SERIES - SHANK NUTS, SELF-LOCKING, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED, FOR 30 DEGREES SWAGE - CLASSIFICATION: 1210 MPA (AT AMBIENT TEMPERATURE)/730 DEGREES C |
PREN 4673-005 : 200P1 | AEROSPACE SERIES - INSERTS, UNJ THREADS, SELF-LOCKING, WITH SELF-BROACHING KEYS - PART 005: IN HEAT RESISTING NICKEL BASE ALLOY - NI-P101HT (WASPALOY), SILVER PLATING |
PREN 3637 : 200P1 | AEROSPACE SERIES - NUTS, SELF-LOCKING, BI-HEXAGONAL (DOUBLE REDUCED), IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATED - CLASSIFICATION: 1210 MPA/730 DEGREES C |
EN 4124:2018 | Aerospace series - Shank nuts, self-locking, in heat resisting nickel base alloy NI-PH1302 (Waspaloy), silver plated on thread, for 60° swage - Classification: 1 210 MPa (at ambient temperature) / 730 °C |
BS EN 4624:2010 | Aerospace series. Inserts, MJ threads, self-locking, with self-broaching keys, in heat resisting nickel base alloy NI-PH1302 (Waspaloy), silver plate |
05/30141105 DC : 0 | EN 4624 - AEROSPACE SERIES - INSERTS, MJ THREADS, SELF-LOCKING, WITH SELF-BROACHING KEYS, IN HEAT RESISTING NICKEL BASE ALLOY NI-P101HT (WASPALOY), SILVER PLATING |
BS EN 4673-005:2010 | Aerospace series. Inserts, UNJ threads, self-locking, with self-broaching keys In heat resisting nickel base alloy NI-P101HT (WASPALOY), silver plating |
PREN 4235-3 : 200P2 | AEROSPACE SERIES - STEEL - WROUGHT PRODUCTS - TECHNICAL SPECIFICATION - PART 3: BAR AND SECTION |
PREN 2043 : 200P1 | AEROSPACE SERIES - METALLIC MATERIALS - GENERAL REQUIREMENTS FOR SEMI-FINISHED PRODUCT QUALIFICATION (EXCLUDING FORGINGS AND CASTINGS) |
PREN 3235-3 : 200P2 | AEROSPACE SERIES - HEAT RESISTING ALLOYS - WROUGHT PRODUCTS - TECHNICAL SPECIFICATION - PART 3: BAR AND SECTION |
PREN 4500-003 : 200P2 | AEROSPACE SERIES - METALLIC MATERIALS - RULES FOR DRAFTING AND PRESENTATION OF MATERIAL STANDARDS - PART 003: SPECIFIC RULES FOR HEAT RESISTING SLLOYS |
EN 4258:1998 | Aerospace series - Metallic materials - General organization of standardization - Links between types of EN standards and their use |
Please Login or Create an Account so you can add users to your Multi user PDF Later.
Important note : All end users must be registered with an Account prior to user licenses being assigned.
Users cannot be edited or removed once added to your Multi user PDF.
Access your standards online with a subscription
Features
-
Simple online access to standards, technical information and regulations.
-
Critical updates of standards and customisable alerts and notifications.
-
Multi-user online standards collection: secure, flexible and cost effective.